Fatigue fracture behaviours of the bond zone of local reinforced components

X. H. Zhang; W. Z. Zhang

Fatigue fracture behaviours of the bond zone of local reinforced components

X. H. Zhang^*
, W. Z. Zhang

^*Corresponding author for this work

School of Mechanical Engineering

Beijing Institute of Technology

Research output: Contribution to conference › Paper › peer-review

Abstract

Al-Si alloys locally reinforced by aluminum borate whiskers were fabricated by squeeze casting. The fatigue fracture behaviors of the bond zone between the reinforced composites and unreinforced Al-Si alloys were investigated at elevated temperatures to assess the relevant performance. The results indicated that the bonding state of the bond zone was poor at low temperature while was improved as temperature increasing. This leads to a different fatigue fracture mode for the specimens at various temperatures.

Original language	English
Pages	727-728
Number of pages	2
Publication status	Published - 2017
Event	14th International Conference on Fracture, ICF 2017 - Rhodes, Greece Duration: 18 Jun 2017 → 20 Jun 2017

Conference

Conference	14th International Conference on Fracture, ICF 2017
Country/Territory	Greece
City	Rhodes
Period	18/06/17 → 20/06/17

Cite this

@conference{1199c641b4a4410d9a7f03d11c2a7d61,

title = "Fatigue fracture behaviours of the bond zone of local reinforced components",

abstract = "Al-Si alloys locally reinforced by aluminum borate whiskers were fabricated by squeeze casting. The fatigue fracture behaviors of the bond zone between the reinforced composites and unreinforced Al-Si alloys were investigated at elevated temperatures to assess the relevant performance. The results indicated that the bonding state of the bond zone was poor at low temperature while was improved as temperature increasing. This leads to a different fatigue fracture mode for the specimens at various temperatures.",

author = "Zhang, \{X. H.\} and Zhang, \{W. Z.\}",

note = "Publisher Copyright: {\textcopyright} 2017 ICF 2017 - 14th International Conference on Fracture. All rights reserved.; 14th International Conference on Fracture, ICF 2017 ; Conference date: 18-06-2017 Through 20-06-2017",

year = "2017",

language = "English",

pages = "727--728",

}

TY - CONF

T1 - Fatigue fracture behaviours of the bond zone of local reinforced components

AU - Zhang, X. H.

AU - Zhang, W. Z.

PY - 2017

Y1 - 2017

N2 - Al-Si alloys locally reinforced by aluminum borate whiskers were fabricated by squeeze casting. The fatigue fracture behaviors of the bond zone between the reinforced composites and unreinforced Al-Si alloys were investigated at elevated temperatures to assess the relevant performance. The results indicated that the bonding state of the bond zone was poor at low temperature while was improved as temperature increasing. This leads to a different fatigue fracture mode for the specimens at various temperatures.

AB - Al-Si alloys locally reinforced by aluminum borate whiskers were fabricated by squeeze casting. The fatigue fracture behaviors of the bond zone between the reinforced composites and unreinforced Al-Si alloys were investigated at elevated temperatures to assess the relevant performance. The results indicated that the bonding state of the bond zone was poor at low temperature while was improved as temperature increasing. This leads to a different fatigue fracture mode for the specimens at various temperatures.

UR - https://www.scopus.com/pages/publications/85065995404

M3 - Paper

AN - SCOPUS:85065995404

SP - 727

EP - 728

T2 - 14th International Conference on Fracture, ICF 2017

Y2 - 18 June 2017 through 20 June 2017

ER -

Fatigue fracture behaviours of the bond zone of local reinforced components

Abstract

Conference

Other files and links

Fingerprint

Cite this