Enhanced electrochemical performance of nano-sized LiFePO₄/C synthesized by an ultrasonic-assisted co-precipitation method

A simple and effective method, the ultrasonic-assisted co-precipitation method, was employed to synthesize nano-sized LiFePO₄/C. A glucose solution was used as the carbon source to produce in situ carbon to improve the conductivity of LiFePO₄. Ultrasonic irradiation was adopted to control the size and homogenize the LiFePO₄/C particles. The sample was characterized by X-ray powder diffraction, field-emission scanning electron microscopy (FE-SEM), transmission electron microscopy (TEM) and high-resolution transmission electron microscopy (HRTEM). FE-SEM and TEM show that the as-prepared sample has a reduced particle size with a uniform size distribution, which is around 50 nm. A uniform amorphous carbon layer with a thickness of about 4-6 nm on the particle surface was observed, as shown in the HRTEM image. The electrochemical performance was demonstrated by the charge-discharge test and electrochemical impedance spectra measurements. The results indicate that the nano-sized LiFePO₄/C presents enhanced discharge capacities (159, 147 and 135 mAh g^-1 at 0.1, 0.5 and 2 C-rate, respectively) and stable cycling performance. This study offers a simple method to design and synthesis nano-sized cathode materials for lithium-ion batteries.