T1 - A simple method for preparing porous carbon by PVDC pyrolysis
AU - Xu, Bin
AU - Wu, Feng
AU - Chen, Shi
AU - Cao, Gaoping
AU - Zhou, Zhiming
PY - 2008/3/5
Y1 - 2008/3/5
N2 - A simple method for preparing porous carbon with high surface area was presented in this paper. The homogeneous poly(vinylidene chloride) (PVDC) was used as starting material. After being carbonized at high temperature under the protection of inert atmosphere, porous carbon with surface area higher than 1200 m2/g has been simply prepared without activation or any other additional processes. The effect of carbonization temperature on the microstructure of the porous carbon was investigated by measuring the BET surface area, pore size distribution, XRD and SEM, etc. The electrochemical measurements showed that the PVDC-based carbon exhibits outstanding high volume capacitance (214 F/cm3) and good rate performance, indicating that it is a promising electrode material for electric double layer capacitors.
AB - A simple method for preparing porous carbon with high surface area was presented in this paper. The homogeneous poly(vinylidene chloride) (PVDC) was used as starting material. After being carbonized at high temperature under the protection of inert atmosphere, porous carbon with surface area higher than 1200 m2/g has been simply prepared without activation or any other additional processes. The effect of carbonization temperature on the microstructure of the porous carbon was investigated by measuring the BET surface area, pore size distribution, XRD and SEM, etc. The electrochemical measurements showed that the PVDC-based carbon exhibits outstanding high volume capacitance (214 F/cm3) and good rate performance, indicating that it is a promising electrode material for electric double layer capacitors.
KW - Carbonization
KW - Poly(vinylidene chloride)
KW - Porous carbon
KW - Specific surface area
UR - http://www.scopus.com/inward/record.url?scp=38649127512&partnerID=8YFLogxK
U2 - 10.1016/j.colsurfa.2007.08.042
DO - 10.1016/j.colsurfa.2007.08.042
M3 - Article
AN - SCOPUS:38649127512
SN - 0927-7757
VL - 316
SP - 85
EP - 88
JO - Colloids and Surfaces A: Physicochemical and Engineering Aspects
JF - Colloids and Surfaces A: Physicochemical and Engineering Aspects
IS - 1-3
ER -