TY - JOUR
T1 - Synthesis and characterization of high molecular weight biodegradable poly (hexane-sebacate)
AU - Sun, Jie
AU - Zhang, Wei
AU - Tan, Hui Min
AU - Luo, Yun Jun
PY - 2005/5
Y1 - 2005/5
N2 - High molecular weight biodegradable poly (hexane-sebacate) was synthesized by direct polycondensation from sebacic acid and 1,6-hexanediol, the chemical structure was identified by FT-IR and 1H-NMR, the intrinsic viscosity was measured by Ubbelohde viscometer, the melting point, glass transition temperature was determined by DSC, and the tensile strength is 23.5 MPa, the elongation at break is 935.0%, in the synthesis procedure high molecular weight of product (M̄n=45809) was obtained with the yield of 96%.
AB - High molecular weight biodegradable poly (hexane-sebacate) was synthesized by direct polycondensation from sebacic acid and 1,6-hexanediol, the chemical structure was identified by FT-IR and 1H-NMR, the intrinsic viscosity was measured by Ubbelohde viscometer, the melting point, glass transition temperature was determined by DSC, and the tensile strength is 23.5 MPa, the elongation at break is 935.0%, in the synthesis procedure high molecular weight of product (M̄n=45809) was obtained with the yield of 96%.
KW - Characterization
KW - Direct polycondensation
KW - Poly (hexane-sebacate )
UR - http://www.scopus.com/inward/record.url?scp=20444364212&partnerID=8YFLogxK
M3 - Article
AN - SCOPUS:20444364212
SN - 1000-7555
VL - 21
SP - 96
EP - 98
JO - Gaofenzi Cailiao Kexue Yu Gongcheng/Polymeric Materials Science and Engineering
JF - Gaofenzi Cailiao Kexue Yu Gongcheng/Polymeric Materials Science and Engineering
IS - 3
ER -